Büşra Keskin Neslihana, Güneç Gürkanb
aYildirim Beyazit University, Faculty of Dentistry, Department of Endodontics, Ankara, Turkey
bBeykent University, Faculty of Dentistry, Department of Endodontics, Istanbul, Turkey
Summary
Background/Aim: The aim of the present study was to compare the cyclic fatigue resistance of NiTi files running with reciprocal motion and having different characteristics (RPC Blue, WOG, EndoArt Wise Reciproc Gold, EndoArt Wise Reciproc Blue) at the intracanal temperature (35°C) by using NaOCl irrigation solution. Material and Methods: Totally 60 WaveOne GOLD (Dentsply-Sirona, Ballaigues, Switzerland), Reciproc Blue (VDW, Munich, Germany), EndoArt Wise Reciproc Gold, and EndoArt Wise Blue (Inci Dental Productions Co, Istanbul, Turkey) (n= 15) files were used. Each of the rotary files were tested at the intracanal temperature (35°C) using a dynamic model in a stainless-steel artificial canal with an inner diameter of 1.5 mm, 60° angle of curvature, and 2mm radius of curvature until fracture occurred. The device automatically stopped at the moment of fracture and the number of cycles to the fracture was calculated as per second. The lengths of fractured parts were measured using a digital microcaliper. The One-Way Analysis of Variance (ANOVA) and Tukey’s posthoc tests were used for intergroup comparisons. Results: In 2 mm Radius of curvature, the EndoArt Wise Reciproc Blue group had a significantly higher time to fracture followed by the EndoArt Wise Reciproc Gold, Resiproc Blue, WaveOne Gold. No significant difference was found between EndoArt Wise Reciproc Gold and Resiproc Blue groups (P>0.05). Among the groups, there was no statistically significant difference in the lengths of fractured parts of the instruments (P> 0.05). Conclusions: EndoArt Wise Reciproc Blue files exhibited significantly higher cyclic fatigue resistance compared with other files tested in a 2-mm radius of curvature and a 600 angle in an artificial canal at the intracanal temperature.
Keywords: NiTi; cyclic fatigue; EndoArt Wise Reciproc Blue; WaveOne Gold; EndoArt Wise Reciproc Gold
Reference
Ahn, S.Y., Kim, H.C., Kim, E.C. (2016) Kinematic effects of nickel-titanium instruments with reciprocating or continuous rotation motion: A systematic review of in vitro studies. Journal of Endodontics, 42(7): 1009-1017
Alcalde, M.P., Duarte, M.A.H., Bramante, C.M., de Vasconselos, B.C., Tanomaru-Filho, M., Guerreiro-Tanomaru, J.M., et al. (2018) Cyclic fatigue and torsional strength of three different thermally treated reciprocating nickel-titanium instruments. Clinical Oral Investigations, 22(4): 1865-1871
Al-Obaida, M.I., Merdad, K., Alanazi, M.S., Altwaijry, H., Alfaraj, M., Alkhamis, A.A., Al-Madi, E.M. (2019) Comparison of cyclic fatigue resistance of 5 heat-treated nickel-titanium reciprocating systems in canals with single and double curvatures. Journal of Endodontics, 45(10): 1237-1241
Cheung, G.S.P., Darvell, B.W. (2007) Low-cycle fatigue of NiTi rotary instruments of various cross-sectional shapes. International Endodontic Journal, 40(8): 626-632
Craveiro, de M.C.M., de Azevedo, B.G.M., Buono, L.V.T. (2002) Fatigue resistance of engine-driven rotary nickel-titanium endodontic instruments. J Endod, 28: 765-769
de Hemptinne, F., Slaus, G., Vandendael, M., Jacquet, W., de Moor, R.J., Bottenberg, P.J. (2015) In vivo intracanal temperature evolution during endodontic treatment after the injection of room temperature or preheated sodium hypochlorite. Journal of Endodontics, 41(7): 1112-1115
De-Deus, G., Moreira, E.J.L., Lopes, H.P., Elias, C.N. (2010) Extended cyclic fatigue life of F2 ProTaper instruments used in reciprocating movement. International Endodontic Journal, 43(12): 1063-1068
De-Deus, G., Silva, E.J.N.L., Vieira, V.T.L., Belladonna, F.G., Elias, C.N., Plotino, G., Grande, N.M. (2017) Blue thermomechanical treatment optimizes fatigue resistance and flexibility of the reciproc files. Journal of Endodontics, 43(3): 462-466
De-Deus, G., Leal, V.V.T., Nogueira, D.S.E.J., Lopes, H., Elias, C.N., Moreira, E.J. (2014) Bending resistance and dynamic and static cyclic fatigue life of Reciproc and WaveOne large instruments. Journal of Endodontics, 40(4): 575-579
Elnaghy, A.M., Elsaka, S.E. (2017) Effect of sodium hypochlorite and saline on cyclic fatigue resistance of WaveOne Gold and Reciproc reciprocating instruments. International Endodontic Journal, 50(10): 991-998
Ferreira, F., Adeodato, C., Barbosa, I., Aboud, L., Scelza, P., Zaccaro, S.M. (2017) Movement kinematics and cyclic fatigue of NiTi rotary instruments: A systematic review. International Endodontic Journal, 50(2): 143-152
Fishelberg, G., Pawluk, J.W. (2004) Nickel-titanium rotary-file canal preparation and intracanal file separation. Compend Contin Educ Dent, 25: 17-18
Gao, Y., Gutmann, J.L., Wilkinson, K., Maxwell, R., Ammon, D. (2012) Evaluation of the impact of raw materials on the fatigue and mechanical properties of ProFile Vortex rotary instruments. Journal of Endodontics, 38(3): 398-401
Grande, N.M., Plotino, G., Silla, E., Pedullà, E., Dedeus, G., Gambarini, G., Somma, F. (2017) Environmental temperature drastically affects flexural fatigue resistance of nickel-titanium rotary files. Journal of Endodontics, 43(7): 1157-1160
Gündoğar, M., Özyürek, T. (2017) Cyclic fatigue resistance of OneShape, HyFlex EDM, WaveOne Gold, and Reciproc Blue nickel-titanium instruments. Journal of Endodontics, 43(7): 1192-1196
Haïkel, Y., Serfaty, R., Bateman, G., Senger, B., Allemann, C. (1999) Dynamic and cyclic fatigue of engine-driven rotary nickel-titanium endodontic instruments. Journal of Endodontics, 25(6): 434-440
Jamleh, A., Alghaihab, A., Alfadley, A., Alfawaz, H., Alqedairi, A., Alfouzan, K. (2019) Cyclic fatigue and torsional failure of EdgeTaper platinum endodontic files at simulated body temperature. Journal of Endodontics, 45(5): 611-614
Keleş, A., Eymirli, A., Uyanık, O., Nagas, E. (2019) Influence of static and dynamic cyclic fatigue tests on the lifespan of four reciprocating systems at different temperatures. International Endodontic Journal, 52(6): 880-886
Keles, A., Uzunoglu, O.E., Uyanik, M.O., Nagas, E. (2019) Effect of temperature of sodium hypochlorite on cyclic fatigue resistance of heat-treated reciprocating files. Journal of Endodontics, 45(2): 205-208
Keskin, C., Inan, U., Demiral, M., Keleş, A. (2017) Cyclic fatigue resistance of Reciproc Blue, Reciproc, and WaveOne Gold reciprocating instruments. Journal of Endodontics, 43(8): 1360-1363
Klymus, M.E., Alcalde, M.P., Vivan, R.R., Só, M.V.R., de Vasconselos, B.C., Duarte, M.A.H. (2019) Effect of temperature on the cyclic fatigue resistance of thermally treated reciprocating instruments. Clinical Oral Investigations, 23(7): 3047-3052
Lopes, H.P., Elias, C.N., Vieira, M.V.B., Siqueira, J.F., Mangelli, M., Lopes, W.S.P., Vieira, V.T.L., Alves, F.R.F., Oliveira, J.C.M., Soares, T.G. (2013) Fatigue life of Reciproc and Mtwo instruments subjected to static and dynamic tests. Journal of Endodontics, 39(5): 693-696
Mounce, R. (2004) Rotary nickel titanium instrumentation: A literature review. Dent Today, 23: 119-120
Otsuka, K., Ren, X. (2005) Physical metallurgy of Ti-Ni-based shape memory alloys. Progress in Materials Science, 50(5): 511-678
Ozyurek, T. (2016) Cyclic fatigue resistance of Reciproc, WaveOne, and WaveOne Gold nickel-titanium instruments. J Endod, 42: 1536-1539
Parashos, P., Messer, H.H. (2006) Rotary NiTi instrument fracture and its consequences. Journal of Endodontics, 32(11): 1031-1043
Pedullà, E., Grande, N.M., Plotino, G., Gambarini, G., Rapisarda, E. (2013) Influence of continuous or reciprocating motion on cyclic fatigue resistance of 4 different nickel-titanium rotary instruments. Journal of Endodontics, 39(2): 258-261
Peters, O.A., Barbakow, F. (2002) Dynamic torque and apical forces of ProFile.04 rotary instruments during preparation of curved canals. International Endodontic Journal, 35(4): 379-389
Plotino, G., Grande, N.M., Testarelli, L., Gambarini, G., Castagnola, R., Rossetti, A., Özyürek, T., Cordaro, M., Fortunato, L. (2018) Cyclic fatigue of reciproc and Reciproc Blue nickel-titanium reciprocating files at different environmental temperatures. Journal of Endodontics, 44(10): 1549-1552
Plotino, G., Grande, N.M., Mercadé, B.M., Testarelli, L., Gambarini, G. (2017) Influence of temperature on cyclic fatigue resistance of ProTaper Gold and ProTaper universal rotary files. Journal of Endodontics, 43(2): 200-202
Pruett, J.P., Clement, D.J., Carnes, D.L. (1997) Cyclic fatigue testing of nickel-titanium endodontic instruments. Journal of Endodontics, 23(2): 77-85
Rodrigues, R.C.V., Lopes, H.P., Elias, C.N., Amaral, G., Vieira, V.T.L., de Martin, A.S. (2011) Influence of different manufacturing methods on the cyclic fatigue of rotary nickel-titanium endodontic instruments. Journal of Endodontics, 37(11): 1553-1557
Shen, Y., Zhou, H.M., Zheng, Y.F., Peng, B., Haapasalo, M. (2013) Current challenges and concepts of the thermomechanical treatment of nickel-titanium instruments. Journal of Endodontics, 39(2): 163-172
Silva, E.J.N.L., Vieira, V.T.L., Hecksher, F., Dos, S.O.M.R.S., Dos, S.A.H., Moreira, E.J.L. (2018) Cyclic fatigue using severely curved canals and torsional resistance of thermally treated reciprocating instruments. Clinical Oral Investigations, 22(7): 2633-2638
Topcuoglu, H.S., Duzgun, S., Akti, A., Topcuoglu, G. (2017) Laboratory comparison of cyclic fatigue resistance of WaveOne Gold, Reciproc and WaveOne files in canals with a double curvature. Int Endod J, 50: 713-717
Tripi, T.R., Bonaccorso, A., Condorelli, G.G. (2006) Cyclic fatigue of different nickel-titanium endodontic rotary instruments. Oral Surgery, Oral Medicine, Oral Pathology, and Oral Radiology, 102: 106-114
Wei, X., Ling, J., Jiang, J., Huang, X., Liu, L. (2007) Modes of failure of ProTaper nickel-titanium rotary instruments after clinical use. Journal of Endodontics, 33(3): 276-279
You, S., Bae, K., Baek, S., Kum, K., Shon, W., Lee, W. (2010) Lifespan of one nickel-titanium rotary file with reciprocating motion in curved root canals. Journal of Endodontics, 36(12): 1991-1994
Zehnder, M. (2006) Root canal irrigants. Journal of Endodontics, 32(5): 389-398
Zupanc, J., Vahdat-Pajouh, N., Schäfer, E. (2018) New thermomechanically treated NiTi alloys: A review. International Endodontic Journal, 51(10): 1088-1103
Balkan Journal of Dental Medicine, 2021, vol. 25, br. 2, str. 87-91